Effect of coatings on long term behaviour of a commercial stainless steel for solid oxide electrolyser cell interconnect application in H2 /H2O atmos…
2014
Abstract K41X (AISI 441) stainless steel evidenced a high electrical conductivity after 3000 h ageing in H 2 /H 2 O side when used as interconnect for solid oxide electrolyser cells (SOEC) working at 800 °C. Perovskite (La 1 − x Sr x MnO 3 − δ ) and spinel (Co 3 O 4 ) oxides coatings were applied on the surface of the ferritic steel for ageing at 800 °C for 3000 h. Both coatings improved the behaviour of the steel and give interesting opportunities to use the K41X steel as interconnect for hydrogen production via high temperature steam electrolysis. Co 3 O 4 reduced into Co leading to a very good Area Specific Resistance (ASR) parameter, 0.038 Ω cm 2 . Despite a good ASR (0.06 Ω cm 2 ), La …
Dual atmosphere study of the K41X stainless steel for interconnect application in high temperature water vapour electrolysis
2015
Abstract High temperature water vapour electrolysis (HTE) is one of the most efficient technologies for mass hydrogen production. A major technical difficulty related to high temperature water vapour electrolysis is the development of interconnects working efficiently for a long period. Working temperature of 800 °C enables the use of metallic materials as interconnects. High temperature corrosion behaviour and electrical conductivity of a commercial stainless steel, K41X (AISI 441), were tested in HTE dual atmosphere (95%O 2 -5%H 2 0/10%H 2 -90%H 2 O) at 800 °C. The alloy exhibits a very good oxidation resistance compared to single atmosphere tests. However, a supplied electrical current s…
High-Temperature Electrolysis of Kraft Lignin for Selective Vanillin Formation
2020
Lignin represents the largest renewable resource of aromatic moieties on earth and harbors a huge potential as a sustainable feedstock for the synthesis of biobased aromatic fine chemicals. Due to the complex, heterogeneous, and robust chemical structure of the biopolymer, the valorization is associated with significant challenges. Unfortunately, technical lignins, which are a large side stream of the pulp and paper industries, are mainly thermally exploited. In this study, technical Kraft lignin was selectively electrochemically depolymerized to the aroma chemical vanillin. Using electricity, toxic and/or expensive oxidizers could be replaced. The electrodegradation of Kraft lignin was per…
Coated interconnects development for high temperature water vapour electrolysis: Study in anode atmospher
2013
International audience; High temperature water vapour electrolysis (HTE) is an efficient technology for hydrogen production. In this context, a commercial stainless steel, K41X (AISI 441), was chosen as interconnect. In a previous paper, the high temperature corrosion and the electrical conductivity were evaluated in both anode (O-2-H2O) and cathode (H-2-H2O) atmosphere at 800 degrees C. In O-2-H2O atmosphere, the formation of a thin chromia protective layer was observed. Nevertheless, the ASR parameter measured was higher than the maximum accepted value. These results, in addition with chromium evaporation measurements, proved that the K41X alloy is not suitable for HTE interconnect applic…
Evaluation of a new Cr-free alloy as interconnect material for hydrogen production by high temperature water vapour electrolysis: Study in cathode at…
2012
International audience; For economic and ecological reasons, hydrogen is considered as a major energetic vector for the future. Hydrogen production via high temperature water vapour electrolysis (HTE) is a promising technology. A major technical difficulty related to high temperature water vapour electrolysis is the development of interconnects working efficiently for a long period. Working temperature of 800 degrees C enables the use of metallic materials as interconnects. High temperature corrosion behaviour and electrical conductivity of a new Cr-free Fe-Ni-Co alloy were tested in cathode atmosphere (H-2/H2O) at 800 degrees C. The alloy exhibits a poor oxidation resistance but an excelle…
Optimisation of metallic interconnects for hydrogen production by high temperature water vapour electrolysis
2012
For economical and environmental reasons, hydrogen is considered as a major energetic vector for the future. Hydrogen production via high temperature water vapour electrolysis (HTE) is a promising technology. A major technical difficulty related to high temperature water vapour electrolysis is the development of interconnects working efficiently for a long period. Working temperature of 800°C enables the use of metallic materials as interconnects. Chromia forming alloys are among the best candidates. The interconnect material chosen in the present study is a ferritic stainless steel with 18% chromium content. High temperature corrosion resistance and electrical conductivity of the alloy was…